Chemically amplified positive resist composition, a haloester derivative and a process for producing the same

ABSTRACT

The present invention provides a chemically amplified positive resist composition comprising
     (A) a resin which comprises   (i) at least one structural unit selected from the group consisting of structural units of the formulas (no and (V), (ii) a structural unit of the formula (I) and (iii) a structural unit of the formula (II), and   (B) an acid generator.   

     The present invention also provides a haloester derivative of the formula (XXI) and a process for producing the same

This nonprovisional application claims priority under 35 U.S.C. § 119(a) on patent application No. 2004-140709 filed in JAPAN on May 11, 2004, the entire contents of which are hereby incorporated by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a chemically amplified positive resist composition used in fine processing of semiconductors, a component resin in the composition, a haloester derivative for the component resin and a process for producing the haloester derivative.

2. Related Art

Semiconductor microfabrication employs a lithography process using a resist composition. In lithography, theoretically, the shorter the exposure wavelength becomes, the higher the resolution can be made, as expressed by Rayleigh's diffraction limit formula. The wavelength of an exposure light source for lithography used in the manufacture of semiconductor devices has been shortened year by year as g line having a wavelength of 436 nm, i line having a wavelength of 365 nm, KrF excimer laser having a wavelength of 248 nm and ArF excimer laser having a wavelength of 193 nm. F₂ excimer laser having a wavelength of 157 nm seems to be the next-generation exposure light source. Further, as the exposure light source of the subsequent generation, soft X ray (EUV) having a wavelength of 13 nm or shorter has been proposed as the exposure light source following the 157 nm-wavelength F₂ excimer laser.

As line width has become narrower in lithography process using light sources having shorter wavelength, such as excimer laser and the like, especially line edge roughness (roughness of pattern surfaces or wave of pattern, abbreviated by LER), as well as resolution, sensitivity and pattern shape, has become important subject (e.g. Proc. of SPIE Vol. 5038 (2003), 689–698).

After forming patterns by application of the resist composition, exposure of light, and development, there exists a technique adding a step narrowing width of hollows and diameter of holes to make patterns finer by high temperature baking to swell the resist (e.g. JP-A-H09-213603). Hereinafter, the step described above may be referred to as “Reflow Step”.

With further advance of microfabrication technology, it is required for new photoresist compositions to show more advantageous abilities than conventional photoresists. Specifically, photoresist compositions giving better resolution, sensitivity, pattern profiles to resist pattern obtained therefrom, especially giving better line edge roughness are required. Under certain circumstances, further, photoresist compositions capable of giving finer patterns by Reflow Step are required.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a chemically amplified resist composition suitable for ArF excimer laser lithography, showing excellent various resist abilities such as resolution, sensitivity, pattern shape and the like, and giving particularly excellent line edge roughness, and capable of giving finer patterns by Reflow Step.

Another object of the present invention is to provide a new compound for a component resin in the resist composition.

Yet another object of the present invention is to provide a production method for the compound for the component resin.

These and other objects of the present invention will be apparent from the following description.

The present invention relates to the followings:

-   <1> A chemically amplified positive resist composition comprising -   (A) a resin which comprises -   (i) at least one structural unit selected from the group consisting     of structural units of the formulas (IV) and (V)

-    wherein X³ and X⁴ each independently represents a hydrogen atom, an     alkyl group having 1 to 4 carbon atoms or a perfluoroalkyl group     having 1 to 4 carbon atoms, Z³ and Z⁴ each independently represents     a divalent hydrocarbon group having 1 to 12 carbon atoms, n³ and n⁴     each independently represents an integer of 0 to 3, R² and R³ each     independently represents a hydroxyl group or a hydroxymethyl group,     G represents —(CO)O— or —O—, R⁴ represents an alkyl group having 1     to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, and     p and q each independently represents an integer of 0 to 2, -   (ii) a structural unit of the formula (I)

-    wherein X represents a hydrogen atom, an alkyl group having 1 to 4     carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms, Z     represents a divalent hydrocarbon group having 1 to 12 carbon atoms,     R represents an alkyl group having 1 to 6 carbon atoms, and m     represents an integer of 0 to 2, and -   (iii) a structural unit of the formula (II)

-    wherein X¹ represents a hydrogen atom, an alkyl group having 1 to 4     carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms,     Z¹ represents a divalent hydrocarbon group having 1 to 12 carbon     atoms, n¹ represents an integer of 0 to 3, R¹ represents an alkyl     group having 1 to 6 carbon atoms or a cycloalkyl group having 3 to     12 carbon atoms, and Y represents at least two atoms necessary to     form an alicyclic hydrocarbon group together with the adjacent     carbon atom, and -   (B) an acid generator. -   <2> The composition according to <1>, which further comprises a     structural unit of the formula (III)

-    wherein X² represents a hydrogen atom, an alkyl group having 1 to 4     carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms,     Z² represents a divalent hydrocarbon group having 1 to 12 carbon     atoms, n² represents an integer of 0 to 3, and A represents a     hydrocarbon group having 1 to 12 carbon atoms. -   <3> The composition according to <1> or <2>, wherein in the     structural unit of the formula (IV), Z³ is a methylene group, an     ethylene group, a trimethylene group or a tetramethylene group, n³     is 0 or 1, and p is 0 or 1, -   in the structural unit of the formula (V), Z⁴ is a methylene group,     an ethylene group, a trimethylene group or a tetramethylene group,     n⁴ is 0 or 1, R4 is a methyl group, an ethyl group, a methoxy group     or an ethoxy group, and q is 0 or 1, -   in the structural unit of the formula (I), Z is a methylene group,     an ethylene group, a trimethylene group or a tetramethylene group,     and m is 0 or 1, and -   in the structural unit of the formula (II), Z¹ is a methylene group,     an ethylene group, a trimethylene group or a tetramethylene group,     n¹ is 0 or 1. -   <4> The composition according to any of <1> to <3>, wherein the     structural unit of the formula (IV) is a structural unit of the     formula (XIV)

-    wherein X¹⁰ represents a hydrogen atom, a methyl group or a     trifluoromethyl group, n¹⁰ represents 0 or 1, and p′ represents 0 or     1, -   the structural unit of the formula (V) is a structural unit of the     formula (XV)

-    wherein X¹¹ represents a hydrogen atom, a methyl group or a     trifluoromethyl group, G represents —(CO)O— or —O—, and n¹¹     represents 0 or 1, -   in the structural unit of the formula (I), Z is a methylene group     and m is 0, and in the structural unit of the formula (II), Z¹ is a     methylene group, n1 is 0 or 1, Y is a divalent hydrocarbon group to     form a divalent adamantane skeleton together with the adjacent     carbon atom, a divalent hydrocarbon group to form a divalent     norbornane skeleton together with the adjacent carbon atom, a     tetramethylene group or a pentamethylene group. -   <5> The composition according to any of <1> to <4>, wherein the     structural unit of the formula (IV) is a structural unit of the     formula (XVIII)

-    wherein X¹² represents a hydrogen atom or a methyl group, and q′     represents 0 or 1, -   the structural unit of the formula (V) is a structural unit of the     formula (XL)

-    wherein X¹³ represents a hydrogen atom or a methyl group, -   the structural unit of the formula (I) is a structural unit of the     formula (XI)

-    wherein X⁶ represents a hydrogen atom, a methyl group or a     trifluoromethyl group, and -   the structural unit of the formula (II) is a structural unit of the     formula (XVII)

-    wherein X⁹⁰ represents a hydrogen atom or a methyl group, R⁹⁰     represents a methyl group, an ethyl group or an isopropyl group, and     Y⁹⁰ is a divalent hydrocarbon group to form a divalent adamantane     skeleton together with the adjacent carbon atom, a tetramethylene     group or a pentamethylene group. -   <6> The composition according to any of <2> to <5> wherein in the     formula (III), X² is a hydrogen atom, a methyl group or a     trifluoromethyl group, Z² is a methylene group, an ethylene group, a     trimethylene group or a tetramethylene group, n² is 0 or 1, A is an     alkyl having 1 to 5 carbon atoms, an alicyclic hydrocarbon group     having 5 to 12 carbon atoms or an aromatic hydrocarbon group having     6 to 12 carbon atoms. -   <7> The composition according to any of <2> to <6>, wherein in the     formula (III), X² is a hydrogen atom, a methyl group or a     trifluoromethyl group, Z² is a methylene group, n² is 0 or 1, and A     is a methyl group, an ethyl group, a n-propyl group, a n-butyl     group, an isobutyl group, a tert-butyl group, a cyclopentyl group, a     cyclohexyl group, a norbornyl group, an adamantly group or a     decahydro-1,4:5,8-dimethanonaphtyl group. -   <8> A haloester derivative of the formula (XXI)

-    wherein W^(1′) represents a chlorine atom, a bromine atom or an     iodine atom, Z represents a divalent hydrocarbon group having 1 to     12 carbon atoms, R represents an alkyl group having 1 to 6 carbon     atoms, and m represents an integer of 0 to 2. -   <9> A process for producing a haloester derivative of the formula     (XXI)

-    wherein W^(1′) represents a chlorine atom, a bromine atom or an     iodine atom, Z represents a divalent hydrocarbon group having 1 to     12 carbon atoms, R represents an alkyl group having 1 to 6 carbon     atoms, and m represents an integer of 0 to 2, -   which comprises reacting an alcohol derivative of the formula (XX)

-    wherein R and m have the same meanings as defined above, with a     halocarboxylic halide of the formula (XXII)     W^(1′)-Z-CO—W^(2′)  (XXII) -    wherein W^(2′) represents a chlorine atom, a bromine atom or an     iodine atom, and -    W^(1′) and Z have the same meanings as defined above,     in the presence of a deacidifying agent.

DESCRIPTION OF PREFERRED EMBODIMENTS

The present composition is useful for a chemically amplified positive resist composition comprising

-   (A) a resin which comprises -   (i) at least one structural unit selected from the group consisting     of structural units of the formulas (IV) and (V)

-    wherein X³ and X⁴ each independently represents a hydrogen atom, an     alkyl group having 1 to 4 carbon atoms or a perfluoroalkyl group     having 1 to 4 carbon atoms, Z³ and Z⁴ each independently represents     a divalent hydrocarbon group having 1 to 12 carbon atoms, n³ and n⁴     each independently represents an integer of 0 to 3, R² and R³ each     independently represents a hydroxyl group or a hydroxymethyl group,     G represents —(CO)O— or —O—, R⁴ represents an alkyl group having 1     to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, and     p and q each independently represents an integer of 0 to 2, -   (ii) a structural unit of the formula (I)

-    wherein X represents a hydrogen atom, an alkyl group having 1 to 4     carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms, Z     represents a divalent hydrocarbon group having 1 to 12 carbon atoms,     R represents an alkyl group having 1 to 6 carbon atoms, and m     represents an integer of 0 to 2, and -   (iii) a structural unit of the formula (II)

-    wherein X¹ represents a hydrogen atom, an alkyl group having 1 to 4     carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms,     Z¹ represents a divalent hydrocarbon group having 1 to 12 carbon     atoms, n¹ represents an integer of 0 to 3, R¹ represents an alkyl     group having 1 to 6 carbon atoms or a cycloalkyl group having 3 to     12 carbon atoms, and Y represents at least two atoms necessary to     form an alicyclic hydrocarbon group together with the adjacent     carbon atom, and -   (B) an acid generator.

Hereinafter, “a resin which comprises (i) at least one structural unit selected from the group consisting of structural units of the formulas (IV) and (V), (ii) a structural unit of the formula (I) and (iii) a structural unit of the formula (II) may be referred to as “RESIN”.

RESIN preferably further contains a structural unit of the formula (III)

-    wherein X² represents a hydrogen atom, an alkyl group having 1 to 4     carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms,     Z² represents a divalent hydrocarbon group having 1 to 12 carbon     atoms, n² represents an integer of 0 to 3, and A represents a     hydrocarbon group having 1 to 12 carbon atoms.

RESIN in the present composition may contain plural kinds of the structural unit of the formula (II), and also may contain plural kinds of any other structural unit(s).

RESIN itself is usually insoluble or poorly soluble in an alkali aqueous solution but becomes soluble in an alkali aqueous solution by the action of an acid. Specifically some group(s) in structural unit(s) constructing RESIN is (are) dissociated by an acid, and the resin component becomes soluble in an alkali aqueous solution after the dissociation.

In the structural unit of the formula (IV), X³ represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, and the like, or a perfluoroalkyl group having 1 to 4 carbon atoms such as a trifluoromethyl group, a pentafluoroethyl group. Z³ represents a divalent hydrocarbon group having 1 to 12 carbon atoms, and examples thereof include alkylene groups such as a methylene group, ethylidene group, a propylidene group, and the like; polymethylene groups such as an ethylene group, a propylene group, a 1,2-butylene group, a trimethylene group, a tetramethylene group, a pentamethylene group, a hexamethylene group, a heptamethylene group, an octamethylene group, a dodecamethylene group, a 1,1-dimethyltrimethylene group, a 1,1-dimethyltetramethylene group, and the like; groups shown by —Pm-Cy-such as

and the like, wherein Pm represents an optionally substituted (poly)methylene group having 1 to 4 carbon atoms and Cy represents a cycloalkan-diyl group having 3 to 8 carbon atoms. n³ represents an integer of 0 to 3. R² and R³ each independently represents a hydroxyl group or a hydroxymethyl group. p represents an integer of 0 to 2.

Specific examples of the structural unit of the formula (IV) include the followings:

As described later in the production method of RESIN in detail, the structural unit of the formula (IV) can be formed by polymerizing a (meth)acrylic derivative of the formula (V)

-    wherein X³, R², R³, Z³, n³ and p have the same meanings as defined     above.

When n³ in the formula XXV is an integer of 1 to 3, the (meth)acrylic derivative of the formula (XXV) can be obtained by reacting an alcohol derivative of the formula (XXVII) with an acid halide derivative of the formula (XXX) to obtain a condensate,

and reacting the condensate with a carboxylic acid derivative of the formula (XXXI) in the presence of a deacidifying agent according to the following equation. In the equation, W¹ and W² each independently represents a chlorine atom, a bromine atom or an iodine atom, n³³ represents an integer of 0 to 2, X³, Z³, n³, R², R³ and p have the same meanings as defined above.

Examples of the alcohol derivatives of the formula (XXVII) include the following compounds:

Examples of the acid halide derivative of the formula (XXX) include the following compounds:

Examples of the carboxylic acid of the formula (XXXI) include an acrylic acid, a methacrylic acid, an α-trifluoromethylmethacrylic acid, and the like.

The reaction between the alcohol derivative of the formula (XXVII) and the acid halide derivative of the formula (XXX) is conducted in, for example, an inert solvent such as toluene, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 100° C. The reaction is preferably conducted in the presence of deacidifying agent. Examples thereof include organic basic compounds such as triethylamine, pyridine, and the like, inorganic basic compounds such as potassium carbonate, sodium hydroxide, and the like, and a mixture of at least two kind thereof can also be used.

The amount of the acid halide derivative of the formula (XXX) is usually 1 to 2 gram equivalent, preferably 1 to 1.5 gram equivalent per one mol of the alcohol derivative of the formula (XXVII). The amount of the deacidifying agent is usually 1 to 5 gram equivalent, preferably 1 to 3 gram equivalent per one mol of the alcohol derivative of the formula (XXVII). The reaction can also be conducted by adding phase transfer catalysts such as tetrabutylammonium bromide, and the like.

The condensate obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

The (meth)acrylic derivative of the formula (XXV) can be produced by reacting the condensate above, which has the formula,

-    wherein W¹, Z³, R², R³, n³ and p have the same meanings as defined     above.     with the carboxylic acid of the formula (XXXI)     in the presence of a deacidifying agent.

The reaction is usually conducted in an inert solvent such as toluene, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 100° C.

Examples of the deacidifying agents include organic basic compounds such as triethylamine, pyridine, and the like, inorganic basic compounds such as potassium carbonate, sodium hydroxide, and the like, and a mixture of at least two kind thereof can also be used.

The amount of the carboxylic acid of the formula (XXXI) is usually 1 to 2 gram equivalent, preferably 1 to 1.5 gram equivalent per one mol of the condensate. The amount of the deacidifying agent is usually 1 to 5 gram equivalent, preferably 1 to 3 gram equivalent per one mol of the condensate. The reaction can also be conducted by adding phase transfer catalysts such as tetrabutylammonium bromide, and the like.

The (meth)acrylic derivative of the formula (XXV) obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

The (meth)acrylic derivative of the formula (XXV) can also be obtained by reacting the alcohol derivative of the formula (XXVII) with a carboxylic acid derivative of the formula (XXVI)

-    wherein X³, Z³ and n³ have the same meanings as defined above, -   preferably in the presence of an acidic catalyst according to the     following equation.

Examples of the carboxylic acid derivatives of the formula (XXVI) include the following compounds:

The reaction is an esterification reaction by dehydration of the alcohol derivative of the formula (XXVII) and the carboxylic acid derivative of the formula (XXVI), and is usually conducted in an inert solvent such as toluene, dichloroethane, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 150° C.

When the reaction is conducted by co-distillation dehydration, an acidic catalyst is preferably added. Examples thereof include organic acids such as p-toluenesulfonic acid, trifluoroacetic acid, trifluoromethanesulfonic acid, and the like, acidic catalyst resin such as perfluorinated ion-exchange resin (e.g. Nafion®), and a mixture of at least two kind thereof can also be used. Or alternatively, the (meth)acrylic acid derivative of the formula (XXVI) can be used as a acidic catalyst, as a reactant, and as a solvent.

The amount of the (meth)acrylic acid derivative of the formula (XXVI) is usually 1 mol or more, preferably 1 to 1.5 mol per one mol of the alcohol derivative of the formula (XXVII). The amount of the acidic catalyst is usually catalytic amount to one mol, preferably catalytic amount to 0.5 mol per one mol of the alcohol derivative of the formula (XXVII). In the esterification reaction by dehydration, dehydrating agents such as dicyclohexylcarbodiimide can be used instead of the acidic catalysts. When secondary hydroxyl group coexists with primary hydroxyl group, the primary hydroxyl group is preferably inactivated by protecting group such as silyl group.

The (meth)acrylic derivative of the formula (XXV) obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

In the structural unit of the formula (V), X⁴ represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, and the like, or a perfluoroalkyl group having 1 to 4 carbon atoms such as a trifluoromethyl group, a pentafluoroethyl group. Z⁴ represents a divalent hydrocarbon group having 1 to 12 carbon atoms, and examples thereof include alkylene groups such as a methylene group, ethylidene group, a propylidene group, and the like; polymethylene groups such as an ethylene group, a propylene group, a 1,2-butylene group, a trimethylene group, a tetramethylene group, a pentamethylene group, a hexamethylene group, a heptamethylene group, an octamethylene group, a dodecamethylene group, a 1,1-dimethyltrimethylene group, a 1,1-dimethyltetramethylene group, and the like; groups shown by —Pm-Cy-such as

and the like, wherein Pm represents an optionally substituted (poly)methylene group having 1 to 4 carbon atoms and Cy represents a cycloalkan-diyl group having 3 to 8 carbon atoms. n⁴ represents an integer of 0 to 3. G represents —(CO)O— or —O—. R⁴ represents an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, a n-propyl group, an isopropyl group, a n-butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group or an alkoxy group having 1 to 4 carbon atoms such as a methoxy group, an ethoxy group, a n-propoxy group, an isopropoxy group, a n-butoxy group, an isobutoxy group, a sec-butoxy group, a tert-butoxy group, and the like. q represents an integer of 0 to 2.

Specific examples of the structural unit of the formula (V) include the followings:

As described later in the production method of RESIN in detail, the structural unit of the formula (V) can be formed by polymerizing a (meth)acrylic derivative of the formula (XXXIV)

-    wherein X⁴, R⁴, Z⁴, n⁴ and q have the same meanings as defined     above.

The (meth)acrylic derivative of the formula (XXXIV) can be obtained by reacting a γ-butyrolactone derivative of the formula (XXXIII)

-    wherein W³ represents a chlorine atom, and R⁴ and q have the same     meanings as defined above,     with an alcohol derivative of the formula (XXXII) in the presence of     a basic compound,

-    wherein X⁴, Z⁴, G and n⁴ have the same meanings as defined above,     according to the following equation.

Examples of the alcohol derivatives of the formula (XXXII) include the following compounds:

Examples of the γ-butyrolactone derivatives of the formula (XXXIII) include the following compounds:

The reaction between γ-butyrolactone derivative of the formula (XXXIII) and the alcohol derivative of the formula (XXXII) is usually conducted in an inert solvent such as toluene, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 150° C.

It is preferable that a deacidifying agent is added in the reaction. Examples thereof include organic basic compounds such as triethylamine, pyridine, and the like, inorganic basic compounds such as potassium carbonate, sodium hydroxide, and the like, and a mixture of at least two kind thereof can also be used.

The amount of the hydroxy derivative of the formula (XXXII) is usually 1 to 2 mol equivalent, preferably 1 to 1.5 mol equivalent per one mol of the γ-lactone derivative of the formula (XXXIII). The amount of the deacidifying agent is usually 1 to 5 mol equivalent, preferably 1 to 3 mol equivalent per one mol of the γ-lactone derivative of the formula (XXXIII). The reaction can also be conducted by adding phase transfer catalysts such as tetrabutylammonium bromide, and the like.

The (meth)acrylic derivative of the formula (XXXIV) obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

In the structural unit of the formula (I), X represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, and the like, or a perfluoroalkyl group having 1 to 4 carbon atoms such as a trifluoromethyl group, a pentafluoroethyl group. Z represents a divalent hydrocarbon group having 1 to 12 carbon atoms, and examples thereof include alkylene groups such as a methylene group, ethylidene group, a propylidene group, and the like; polymethylene groups such as an ethylene group, a propylene group, a 1,2-butylene group, a trimethylene group, a tetramethylene group, a pentamethylene group, a hexamethylene group, a heptamethylene group, an octamethylene group, a dodecamethylene group, a 1,1-dimethyltrimethylene group, a 1,1-dimethyltetramethylene group, and the like; groups shown by —Pm-Cy-such as

and the like, wherein Pm represents an optionally substituted (poly)methylene group having 1 to 4 carbon atoms and Cy represents a cycloalkan-diyl group having 3 to 8 carbon atoms. R represents an alkyl group having 1 to 6 carbon atoms such as a methyl group, an ethyl group, a n-propyl group, an isopropyl group, a n-butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a n-pentyl group, a isopentyl group, a sec-pentyl group, a tert-pentyl group, a neopentyl group, a n-hexyl group, a sec-hexyl group, isohexyl group, tert-hexyl group, neohexyl group, and the like. m represents an integer of 0 to 2.

Specific examples of the structural unit of the formula (1) include the followings:

As described later in the production method of RESIN in detail, the structural unit of the formula (I) can be formed by polymerizing a (meth)acrylic derivative of the formula (XIX)

-    wherein X, Z, R and m have the same meanings as defined above.

The (meth)acrylic derivative of the formula (XIX) can be obtained by reacting an alcohol derivative of the formula (XX) with an acid halide derivative of the formula (XXII) to obtain a haloester derivative of the formula (XXI), and reacting the haloester of the formula (XXI) with an carboxylic acid of the formula (XXIII) according to the following equation. In the equation, W^(1′) and W^(2′) each independently represents a chlorine atom, a bromine atom or an iodine atom and X, Z and R have the same meanings as defined above.

In the formulas (XIX), (XXIII), (XXI), (XXII) and (I), W^(1′) and W^(2′) are preferably a chlorine atom or a bromine atom, Z is preferably a methylene group, an ethylene group, a trimethylene group or tetramethylene group, R is preferably a methyl group, an ethyl group or an isopropyl group, X is preferably a hydrogen atom, a methyl group or a trifluoromethyl group, and m is preferably 0. More preferably, W^(1′), W^(2′), Z, R, X and m are a chlorine atom; a chlorine atom; a methylene group or an ethylene group; a methyl group or an ethyl group; a hydrogen atom or a methyl group; and 0, respectively.

Examples of the (meth)acrylic derivatives of the formula (XIX) include the following compounds:

As the (meth)acrylic derivative of the formula (XIX), a (meth)acrylic derivative of the formula (XV′) is particularly preferred.

In the formula above, X has the same meaning as defined above.

The (meth)acrylic derivative of the formula (XV′) can be obtained, for example, by reacting a haloester derivative of the formula (XVI)

wherein W¹ has the same meaning as defined above,

-   with (meth)acrylic acid in the presence of a deacidifying agent.

Specific examples of the alcohol derivatives of the formula (XX include the following compounds:

Specific examples of the acid halide derivative of the formula (XXII) include the following compounds:

Specific examples of the haloester derivative of the formula (XX) include the following compounds:

Among the haloester derivative of the formula (XXI), a haloester derivative of the following formula (XVI) is more preferred.

In the formula above, W^(1′) has the same meaning as defined above.

The haloester derivative of the formula (XVI) can be obtained, for example, by reacting an alcohol derivative of the formula (XXXVIII)

with an acid halide derivative of the following formula (XXXVIII) in the presence of a deacidifying agent. W^(1′)—CH₂—CO—W^(2′)  (XXXVIII) In the formula above, W¹ and W² each independently a chlorine atom, a bromine atom or an iodine atom.

Examples of the carboxylic acid of the formula (XXIII) include acrylic acid, methacrylic acid, α-trifluoromethylmethacrylic acid, and the like.

The reaction between the alcohol derivative of the formula (XX) and the acid halide derivative of the formula (XXII) is conducted in, for example, an inert solvent such as toluene, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 100° C. The reaction is preferably conducted in the presence of deacidifying agent. Examples thereof include organic basic compounds such as triethylamine, pyridine, and the like, inorganic basic compounds such as potassium carbonate, sodium hydroxide, and the like, and a mixture of at least two kind thereof can also be used.

The amount of the acid halide derivative of the formula (XXII) is usually 1 to 2 gram equivalent, preferably 1 to 1.5 gram equivalent per one mol of the alcohol derivative of the formula (XX). The amount of the deacidifying agent is usually 1 to 5 gram equivalent, preferably 1 to 3 gram equivalent per one mol of the alcohol derivative of the formula (XX). The reaction can also be conducted by adding phase transfer catalysts such as tetrabutylammonium bromide, and the like.

The haloester derivative of the formula (XXI) obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

The (meth)acrylic derivative of the formula (XIX) can be produced by reacting the haloester derivative of the formula (XXI) above with the carboxylic acid of the formula (XXIII) in the presence of a deacidifying agent.

The reaction is usually conducted in an inert solvent such as toluene, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 100° C.

Examples of the deacidifying agents include organic basic compounds such as triethylamine, pyridine, and the like, inorganic basic compounds such as potassium carbonate, sodium hydroxide, and the like, and a mixture of at least two kind thereof can also be used.

The amount of the carboxylic acid of the formula (XXIII) is usually 1 to 2 gram equivalent, preferably 1 to 1.5 gram equivalent per one mol of the haloester derivative of the formula (XXI). The amount of the deacidifying agent is usually 1 to 5 gram equivalent, preferably 1 to 3 gram equivalent per one mol of the haloester derivative of the formula (XXI). The reaction can also be conducted by adding phase transfer catalysts such as tetrabutylammonium bromide, and the like.

The (meth)acrylic derivative of the formula (XIX) obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

In the structural unit of the formula (II), X¹ represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, and the like, or a perfluoroalkyl group having 1 to 4 carbon atoms such as a trifluoromethyl group, a pentafluoroethyl group. Z¹ represents a divalent hydrocarbon group having 1 to 12 carbon atoms, and examples thereof include alkylene groups such as a methylene group, ethylidene group, a propylidene group, and the like; polymethylene groups such as an ethylene group, a propylene group, a 1,2-butylene group, a trimethylene group, a tetramethylene group, a pentamethylene group, a hexamethylene group, a heptamethylene group, an octamethylene group, a dodecamethylene group, 1,1-dimethyltrimethylene group, a 1,1-dimethyltetramethylene group, and the like; groups shown by —Pm-Cy-such as

and the like, wherein Pm represents an optionally substituted (poly)methylene group having 1 to 4 carbon atoms and Cy represents a cycloalkan-diyl group having 3 to 8 carbon atoms. n¹ represents an integer of 0 to 3. R¹ represents an alkyl group having 1 to 6 carbon atoms such as a methyl group, an ethyl group, an isopropyl group, a n-butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, and the like; or an alicyclic hydrocarbon group having 3 to 12 carbon atoms such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a decahydronaphthyl group, a decahydro-1,4:5,8-dimethanonaphthyl group, and the like. Y has the same meaning as defined above.

Specific examples of the structural unit of the formula (II) include the followings:

As described later in the production method of RESIN in detail, the structural unit of the formula (II) can be formed by polymerizing a (meth)acrylic derivative of the formula (XVIII)

-    wherein X¹, R¹, Y, Z¹ and n¹ have the same meanings as defined     above.

When n¹ in the formula (XXVIII) is an integer of 1 to 3, the (meth)acrylic derivative of the formula (XXVIII) can be produced in the same manner as in the synthetic method of the (meth)acrylic derivative of the formula (XIX) above from the alcohol derivative of the formula (XXIX) according to the following equation.

In the equation, W⁵ and W⁶ each independently represents a chlorine atom, a bromine atom or an iodine atom, nil represents an integer of 0 to 2, X¹, R¹, Y, Z¹ and n¹ have the same meanings as defined above.

The (meth)acrylic derivative of the formula (XXVIII) can also be produced, for example, by reacting the alcohol derivative of the formula (XXIX) with acid halide such as (meth)acrylic chloride in the presence of a deacidifying agent in the same manner as in the synthesis of haloester derivative of the formula (XXI).

Examples of the alcohol derivatives of the formula (XXIX) include the following compounds:

Examples of the acid halide derivatives of the formula (XXXV) include the following compounds.

Examples of the carboxylic acid of the formula (XXXVI) include acrylic acid, methacrylic acid, α-trifluoromethylmethacrylic acid, and the like.

The reaction between the alcohol derivative of the formula (XXIX) and the acid halide derivative of the formula (XXXV) is conducted in, for example, an inert solvent such as toluene, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 100° C., The reaction is preferably conducted in the presence of deacidifying agent. Examples thereof include organic basic compounds such as triethylamine, pyridine, and the like, inorganic basic compounds such as potassium carbonate, sodium hydroxide, and the like, and a mixture of at least two kind thereof can also be used.

The amount of the acid halide derivative of the formula (XXXV) is usually 1 to 2 gram equivalent, preferably 1 to 1.5 gram equivalent per one mol of the alcohol derivative of the formula (XXIX). The amount of the deacidifying agent is usually 1 to 5 gram equivalent, preferably 1 to 3 gram equivalent per one mol of the alcohol derivative of the formula (XXIX). The reaction can also be conducted by adding phase transfer catalysts such as tetrabutylammonium bromide, and the like.

The condensate obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

The (meth)acrylic derivative of the formula (XXVIII) can be produced by reacting the condensate above, which has the formula,

with the carboxylic acid of the formula (XXXVI) in the presence of a deacidifying agent.

The reaction is usually conducted in an inert solvent such as toluene, tetrahydrofuran, dimethylformamide, dimethylsulfoxide, and the like. The reaction temperature is usually −30 to +200° C., preferably 0 to 100° C.

Examples of the deacidifying agents include organic basic compounds such as triethylamine, pyridine, and the like, inorganic basic compounds such as potassium carbonate, sodium hydroxide, and the like, and a mixture of at least two kind thereof can also be used.

The amount of the carboxylic acid of the formula (XXXVI) is usually 1 to 2 gram equivalent, preferably 1 to 1.5 gram equivalent per one mol of the condensate. The amount of the deacidifying agent is usually 1 to 5 gram equivalent, preferably 1 to 3 gram equivalent per one mol of the condensate. The reaction can also be conducted by adding phase transfer catalysts such as tetrabutylammonium bromide, and the like.

The (meth)acrylic derivative of the formula (XXVIII) obtained can be taken out according to the conventional after-treatment and can be purified, for example, by chromatography, recrystallization, distillation, or the like.

In the structural unit of the formula (III), X² represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms such as a methyl group, an ethyl group, and the like, or a perfluoroalkyl group having 1 to 4 carbon atoms such as a trifluoromethyl group, a pentafluoroethyl group. Z² represents a divalent hydrocarbon group having 1 to 12 carbon atoms, and examples thereof include alkylene groups such as a methylene group, ethylidene group, a propylidene group, and the like; polymethylene groups such as an ethylene group, a propylene group, a 1,2-butylene group, a trimethylene group, a tetramethylene group, a pentamethylene group, a hexamethylene group, a heptamethylene group, an octamethylene group, a dodecamethylene group, 1,1-dimethyltrimethylene group, a 1,1-dimethyltetramethylene group, and the like; groups shown by —Pm-Cy-such as

and the like, wherein Pm represents an optionally substituted (poly)methylene group having 1 to 4 carbon atoms and Cy represents a cycloalkan-diyl group having 3 to 8 carbon atoms. n² represents an integer of 0 to 3. A represents a hydrocarbon group having 1 to 12 carbon atoms, examples thereof include alkyl such as a methyl group, an ethyl group, a isopropyl group, n-propyl group, n-butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, and the like, an alicyclic hydrocarbon group having 3 to 12 carbon atoms such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a decahydronaphthyl group, a decahydro-1,4:5,8-dimethanonaphthyl group, and the like.

Specific examples of the structural unit of the formula (III) include the followings:

In the structural unit of the formula (III), X2 is preferably a hydrogen atom, a methyl group or a trifluoromethyl group, Z2 is preferably a methylene group, n2 is preferably 0 or 1, and A is preferably a methyl group, an ethyl group, a n-propyl group, an isopropyl group, a n-butyl group, a t-butyl group, a cyclopentyl group, a cyclohexyl group, a norbornyl group, an adamantyl group or a decahydro-1,4:5,8-dimethanonaphtyl group.

As described later in the production method of RESIN in detail, the structural unit of the formula (III) can be formed by polymerizing a (meth)acrylic derivative of the formula (III′)

-    wherein X², Z², A and n² have the same meanings as defined above.

The (meth)acrylic derivative of the formula (III′) can be produced in the same manner as in the synthetic method of the (meth)acrylic derivative of the formula (XIX) above.

RESIN can be produced by polymerizing at least one monomer selected from the group consisting of (meth)acrylic derivatives of the formulas (XXV) and (XXXIV), (meth)acrylic derivative of the formula (XIX) and (meth)acrylic derivative of the formula (XXVIII), and optionally (meth)acrylic derivative of the formula (III′). Optionally, other monomer(s), such as a monomer which leads to a structural unit having acid-labile group derived from known (meth)acrylate(s), and a monomer which leads to a structural unit not dissociated or not easily dissociated by the action of an acid, as long as the effect of the present invention is not prevented.

Examples of methods for producing RESIN include radical polymerization method, anion polymerization method, coordination polymerization method, and the like, and radical polymerization method is preferred.

As polymerization initiators used therein, the ones effectively generating radicals by heating are preferred. Examples thereof include azo compounds such as 2,2′-azobisisobutyronitrile, dimethyl 2,2′-azobisisobutylate, 2,2′-azobis(2,4-dimethylvaleronitrile), 2,2′-azobis(2-methylbutyronitrile), and the like; organic peroxides such as 2,5-dimethyl-2,5-bis(tert-butylperoxy)hexane, tert-hexyl peroxypivalate, and the like. Each of the polymerization initiator can be used alone or in combination with at least one other kind.

Chain transfer agents such as 1-butanethiol, 2-butanethiol, 1-octanethiol, 1-decanethiol, 1-tetradecanethiol, cyclohexanethiol, 2-methyl-1-propanethiol, and the like, can also be used.

Preferred organic solvents used for the production of RESIN are the ones capable of dissolving all of monomers, polymerization initiators and copolymer obtained. Examples thereof include hydrocarbons such as toluene, and the like, 1,4-dioxane, tetrahydrofuran, methyl isobutyl ketone, isopropyl alcohol, γ-butyrolactone, propylene glycol monomethyl ether acetate, ethyl lactate, and the like. Each of the solvent can be used alone or in combination with at least one other kind.

The polymerization temperature is usually 0 to 150° C., preferably 40 to 100° C.

-   -   The weight average molecular weight of RESIN is preferably 1000         to 500000, and more preferably 4000 to 50000.

RESIN contains usually 1 to 94% by mol, preferably 5 to 60% by mol of the structural unit of the formula (I), usually 1 to 94% by mol, preferably 5 to 60% by mol of at least one monomer selected from the group consisting of the structural units of the formulas (IV) and (V), usually 5 to 98% by mol, preferably 15 to 60% by mol of the structural units of the formula (II), all based on total of structural units in RESIN Total content of the structural units of the formulas (I), (II), (III), (IV) and (V) is generally 70 to 100% by mol, preferably 90 to 100% by mol.

The ratio of each of the structural units can generally be determined by conventional method, for example, by NMR analysis.

For the present composition, RESIN preferably comprises

-   (i) at least one structural unit selected from the group consisting     of the structural units of the formulas (IV) and (V), wherein Z³ is     a methylene group, an ethylene group, a trimmethylene group or a     tetramethylene group, n³ is 0 or 1, p is 0 or 1, Z⁴ is a methylene     group, an ethylene group, a trimmethylene group or a tetramethylene     group, n⁴ is 0 or 1, q is 0 or 1, -   (ii) the structural unit of the formula (I), wherein Z is a     methylene group, an ethylene group, a trimethylene group or a     tetramethylene group, and m is 0, and -   (iii) the structural unit of the formula (II), wherein Z1 is a     methylene group, an ethylene group, a trimethylene group or a     tetramethylene group, n1 is 0 or 1.

RESIN more preferably comprises

-   (i) at least one structural unit selected from the group consisting     of the structural units of the following formulas (XIV) and (XV)

-    wherein X¹⁰ represents a hydrogen atom, a methyl group or a     trifluoromethyl group, nit represents 0 or 1, p′ represents 0 or 1,     X¹¹ represents a hydrogen atom, a methyl group or a trifluoromethyl     group, G represents —(CO)O— or —O—, and n¹¹ represents 0 or 1, -   (ii) the structural unit of the formula (I), wherein Z is a     methylene group, and m is 0, -   (iii) the structural unit of the formula (II), wherein Z1 is a     methylene group, n1 is 0 or 1, and Y is a divalent aliphatic     hydrocarbon group to form an adamantane skeleton together with the     adjacent carbon atom, a divalent aliphatic hydrocarbon group to form     a norbornane skeletone together with the adjacent carbon atom, a     tetramethylene group or a pentamethylene group.

RESIN particularly preferably comprises

-   (i) at least one structural unit selected from the group consisting     of the structural units of the following formulas (XVIII) and (XL)

-    wherein X¹² and X¹³ each independently represents a hydrogen atom,     a methyl group or a trifluoromethyl group, q′ represents 0 or 1, -   (ii) a structural unit of the formula (XI)

wherein X⁶ represents a hydrogen atom, a methyl group or a trifluoromethyl group,

-   (iii) a structural unit of the formula (XVII),

wherein X⁹⁰ represents a hydrogen atom or a methyl group, and R⁹⁰ represents a methyl group, an ethyl group, or an isopropyl group, Y⁹⁰ represents a divalent aliphatic hydrocarbon group to form an adamantane skeleton together with the adjacent carbon atom, a tetramethylene group or a pentamethylene group.

When the structural unit of the formula (III) is contained in RESIN, X2 is more preferably a hydrogen atom, a methyl group or a trifluoromethyl group, Z2 is more preferably a methylene group, n2 is more preferably 0 or 1, and A is more preferably a methyl group, an ethyl group, a n-propyl group, an isopropyl group, a n-butyl group, a t-butyl group, a cyclopentyl group, a cyclohexyl group, a norbornyl group, an adamantyl group or a decahydro-1,4:5,8-dimethanonaphtyl group.

The acid generator, another component of the present composition, is the compound which is decomposed to generate an acid by allowing radioactive ray such as light and electron beam to act on the acid generator itself or a resist composition containing the acid generator. The acid generated from the acid generator acts on RESIN, to dissociate acid-labile group present in RESIN.

Such acid generators include, for example, onium salt, organic halogen compounds, sulfone compounds, sulfonate compounds, and the like.

Specific examples thereof include the followings:

-   diphenyliodonium trifluoromethanesulfonate, -   4-methoxyphenylphenyliodinium hexafluoroantimonate, -   4-inethoxyphenylphenyliodinium trifiuoromethanesulfonate, -   bis(4-tert-butylphenyl)iodonium tetrafluoroborate -   bis(4-tert-butylphenyl)iodonium hexafluorophosphate, -   bis(4-tert-butylphenyl)iodonium hexafluoroantimonate -   bis(4-tert-butylphenyl)iodonium trifluoromethanesulfonate, -   triphenylsulfonium hexafluorophosphate, -   triphenylsulfonium hexafluoroantimonate, -   triphenylsulfonium trifluoromethanesulfonate, -   triphenylsulfonium adamantanemethoxycarbonyldifluoromethylsulfonate,     triphenylsulfonium -   1-(3-hydroxymethyladamantane)methoxycarbonyldifluoromethanesulfonate, -   triphenylsulfonium     1-(hexahydro-2-oxo-3,5-methano-2H-cyclopenta[b]furan-6-yloxycarbonyl)difluoromethanesulfonate, -   triphenylsulfonium     4-oxo-1-adamantyloxycarbonyldifluoromethanesulfonate, -   4-methoxyphenyldiphenylsulfonium hexafluoroantimonate, -   4-methoxyphenyldiphenylsulfonium trifluoromethanesulfonate, -   p-tolyldiphenylsulfonium trifluoromethanesulfonate, -   p-tolyldiphenylsulfonium perfluorobutanesulfonate, -   p-tolyldiphenylsulfonium perfluorooctanesulfonate, -   2,4,6-trimethylphenyldiphenylsulfonium trifluoromethanesulfonate, -   4-tert-butylphenyldiphenylsulfonium trifluoromethanesulfonate, -   4-phenylthiophenyldiphenylsulfonium hexafluorophosphate, -   4-phenylthiophenyldiphenylsulfonium hexafluoroantimonate, -   1-(2-naphtholylmethyl)thiolanium hexafluoroantimonate, -   1-(2-naphtholylmethyl)thiolanium trifluoromethanesulfonate, -   4-hydroxy-1-naphthyldimethylsulfonium hexafluoroantimonate, -   4-hydroxy-1-naphthyldimethylsulfonium trifluoromethanesulfonate, -   cyclohexylmethyl(2-oxocyclohexyl)sulfonium     trifluoromethanesulfonate, -   cyclohexylmethyl(2-oxocyclohexyl)sulfonium perfluorobutanesulfonate, -   cyclohexylmethyl(2-oxocyclohexyl)sulfonium perfluorootcanesulfonate, -   2-oxo-2-phenylethylthiacyclopentanium trifluoromethanesulfonate, -   2-oxo-2-phenylethylthiacyclopentanrium perfluorobutanesulfonate, -   2-oxo-2-phenylethylthiacyclopentanium perfluorooctanesulfonate, -   2-methyl-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2,4,6-tris(trichloromethyl)-1,3,5-triazine -   2-phenyl-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(4-chlorophenyl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(4-methoxyphenyl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(4-methoxy-1-naphthyl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(benzo[d][1,3]dioxolan-5-yl)-4,6-bis(trichloromeythyl)-1,3,5-triazine, -   2-(4-methoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(3,4,5-trimethoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(3,4-dimethoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(2,4-dimethoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(2-methoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(4-butoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   2-(4-pentyloxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, -   1-benzoyl-1-phenylmethyl p-toluenesulfonate (generally called     “benzoin tosylate”), -   2-benzoyl-2-hydroxy-2-phenylethyl p-toluenesulfonate (generally     called α-methylolbenzoin tosylate), -   1,2,3-benzene-tri-yl tris(methanesulfonate), -   2,6-dinitrobenzyl p-toluenesulfonate, -   2-nitrobenzyl p-toluenesulfonate, -   4-nitrobenzyl p-toluenesulfonate, -   diphenyl disulfone, -   di-p-tolyl disulfone -   bis(phenylsulfonyl)diazomethane, -   bis(4-chlorophenylsulfonyl)diazomethane, -   bis(p-tolylsulfonyl)diazomethane, -   bis(4-tert-butylphenylsulfonyl)diazomethane, -   bis(2,4-xylylsulfonyl)diazomethane, -   bis(cyclohexylsulfonyl)diazomethane, -   (benzoyl)(phenylsulfonyl)diazomethane, -   N-(phenylsulfonyloxy)succinimide, -   N-(trifluoromethylsulfonyloxy)succinimide, -   N-(trifluoromethylsulfonyloxy)phthalimide, -   N-(trifluoromethylsulfonyloxy)-5-norbornene-2,3-dicarboxyimide, -   N-(trifluoromethylsulfonyloxy)naphthalimide, -   N-(10-camphorsulfonyloxy)naphthalimide, and the like.

In the present composition, performance deterioration caused by inactivation of acid which occurs due to post exposure delay can be diminished by adding basic compounds, particularly, basic nitrogen-containing organic compounds, for example, amines as a quencher.

Specific examples of such basic nitrogen-containing organic compounds include the ones represented by the following formulas:

In the formulas, T¹² and T¹³ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group or an aryl group. The alkyl group preferably has about 1 to 6 carbon atoms, the cycloalkyl group preferably has about 5 to 10 carbon atoms, and the aryl group preferably has about 6 to 10 carbon atoms. Furthermore, at least one hydrogen atom on the alkyl group, cycloalkyl group or aryl group may each independently be substituted with hydroxyil group, amino group, or alkoxy group having 1 to 6 carbon atoms. At least one hydrogen atom on the amino group may each independently be substituted with alkyl group having 1 to 4 carbon atoms.

T¹⁴, T¹⁵ and T¹⁶ each independently represents a hydrogen atom, an alkyl group, a cycloalkyl group, an aryl group or an alkoxy group. The alkyl group preferably has about 1 to 6 carbon atoms, the cycloalkyl group preferably has about 5 to 10 carbon atoms, the aryl group preferably has about 6 to 10 carbon atoms, and the alkoxy group preferably has about 1 to 6 carbon atoms. Furthermore, at least one hydrogen atom on the alkyl group, cycloalkyl group, aryl group or alkoxy group may each independently be substituted with hydroxyl group, amino group, or alkoxy group having 1 to 6 carbon atoms. At least one hydrogen atom on the amino group may be substituted with alkyl group having 1 to 4 carbon atoms.

T¹⁷ represents an alkyl group or a cycloalkyl group. The alkyl group preferably has about 1 to 6 carbon atoms, and the cycloalkyl group preferably has about 5 to 10 carbon atoms. Furthermore, at least one hydrogen atom on the alkyl group or cycloalkyl group may each independently be substituted with hydroxyl group, amino group, or alkoxy group having 1 to 6 carbon atoms. At least one hydrogen atom on the amino group may be substituted with alkyl group having 1 to 4 carbon atoms.

In the formulas, T¹⁸ represents an alkyl group, a cycloalkyl group or an aryl group. The alkyl group preferably has about 1 to 6 carbon atoms, the cycloalkyl group preferably has about 5 to 10 carbon atoms, and the aryl group preferably has about 6 to 10 carbon atoms. Furthermore, at least one hydrogen atom on the alkyl group, cycloalkyl group or aryl group may each independently be substituted with a hydroxyl group, an amino group, or an alkoxy group having 1 to 6 carbon atoms. At least one hydrogen atom on the amino group may each independently be substituted with alkyl group having 1 to 4 carbon atoms.

However, none of T¹² and T¹³ in the compound represented by the above formula [3] is a hydrogen atom.

A represents an alkylene group, a carbonyl group, an imino group, a sulfide group or a disulfide group. The alkylene group preferably has about 2 to 6 carbon atoms.

Moreover, among T¹²–T¹⁸, in regard to those which can be straight-chained or branched, either of these may be permitted.

T¹⁹, T²⁰ and T²¹ each independently represents a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an aminoalkyl group having 1 to 6 carbon atoms, a hydroxyalkyl group having 1 to 6 carbon atoms or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms, or T¹⁹ and T²⁰ bond to form an alkylene group which forms a lactam ring together with adjacent —CO—N—.

Examples of such compounds include hexylamine, heptylamine, octylamine, nonylamine, decylamine, aniline, 2-, 3- or 4-methylaniline, 4-nitroaniline, 1- or 2-naphtylamine, ethylenediamine, tetramethylenediamine, hexamethylenediamine, 4,4′-diamino-1,2-diphenylethane, 4,4′-diamino-3,3′-dimethyldiphenylmethane, 4,4′-diamino-3,3′-diethyldiphenylmethane, dibutylamine, dipentylamine, dihexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, N-methylaniline, piperidine, diphenylamine, triethylamine, trimethylamine, tripropylamine, tributylamine, tripentylamine, trihexylamine, triheptylamine, trioctylamine, trinonylamine, tridecylamine, methyldibutylamine, methyldipentylamine, methyldihexylamine, methyldicyclohexylamine, methyldiheptylamine, methyldioctylamine, methyldinonylarine, methyldidecylamine, ethyldibutylamine, ethydipentylamine, ethyldihexylaamine, ethydiheptylamine, ethyldioctylamine, ethyldinonylamine, ethyldidecylamine, dicyclohexylmethylamine, tris[2-(2-methoxyethoxy)ethyl]amine, triisopropanolamine, N,N-dimethylaniline, 2,6-isopropylaniline, imidazole, pyridine, 4-methylpyridine, 4-methylmidazole, bipyridine, 2,2′-dipyridylamine, di-2-pyridyl ketone, 1,2-di(2-pyridyl)ethane, 1,2-di(4-pyridyl)ethane, 1,3-di(4-pyridyl)propane, 1,2-bis(2-pyridyl)ethylene, 1,2-bis(4-pyridyl)ethylene, 1,2-bis(2-pyridyloxy)ethane, 4,4′-dipyridyl sulfide, 4,4′-dipyridyl disulfide, 1,2-bis(4-pyridyl)ethylene, 2,2′-dipicolylamine, 3,3′-dipicolylamine, tetramethylammonium hydroxide, tetraisopropylammonium hydroxide, tetrabutylammonium hydroxide, tetra-n-hexylammonium hydroxide, tetra-n-octylammonium hydroxide, phenyltrimethylammonium hydroxide, 3-trifluoromethylphenyltrimethylammonium hydroxide, (2-hydroxyethyl)trimethylammonium hydroxide (so-called “choline”), N-methylpyrrolidone, dimethylimidazole, and the like.

Furthermore, hindered amine compounds having piperidine skeleton as disclosed in JP-A-H11-52575 can be used as quencher.

It is preferable that the present composition contains RESIN in an amount of about 80 to 99.9% by weight and the acid generator in an amount of 0,1 to 20% by weight based on the total amount of RESIN and the acid generator.

When basic compound is used as a quencher, the basic compound is contained preferably in an amount of about 0.001 to 1 part by weight, more preferably in an amount of about 0.01 to 0.3 part by weight based on 100 parts by weight of RESIN.

The present composition can contain, if necessary, various additives in small amount such as a sensitizer, solution suppressing agent, other resins, surfactant, stabilizer, dye and the like, as long as the effect of the present invention is not prevented.

The present composition is usually in the form of a resist liquid composition in which the aforementioned ingredients are dissolved in a solvent, and the resist liquid composition is to be applied onto a substrate such as a silicon wafer by a conventional process such as spin coating. The solvent used here is sufficient to dissolve the aforementioned ingredients, have an adequate drying rate, and give a uniform and smooth coat after evaporation of the solvent and, hence, solvents generally used in the art can be used. In the present invention, the total solid content means total content exclusive of solvents.

Examples thereof include glycol ether esters such as ethyl Cellosolve acetate, methyl Cellosolve acetate and propylene glycol monomethyl ether acetate; ethers such as di(ethylene glycol) dimethyl ether; esters such as ethyl lactate, butyl lactate, amyl lactate and ethyl pyruvate and the like; ketones such as acetone, methyl isobutyl ketone, 2-heptanone and cyclohexanone; cyclic esters such as γ-butyrolactone, and the like. These solvents can be used each alone or in combination of two or more.

A resist film applied onto the substrate and then dried is subjected to exposure for patterning, then heat-treated for facilitating a deblocking reaction, and thereafter developed with an alkali developer. The alkali developer used here may be any one of various alkaline aqueous solutions used in the art, and generally, an aqueous solution of tetramethylammonium hydroxide or (2-hydroxyethyl)trimethylammonium hydroxide (commonly known as “choline”) is often used.

It should be construed that embodiments disclosed here are examples in all aspects and not restrictive. It is intended that the scope of the present invention is determined not by the above descriptions but by appended claims, and includes all variations of the equivalent meanings and ranges to the claims.

The present invention will be described more specifically by way of examples, which are not construed to limit the scope of the present invention. The “%” and “part(s)” used to represent the content of any component and the amount of any material used in the following examples are on a weight basis unless otherwise specifically noted. The weight-average molecular weight of any material used in the following examples is a value found by gel permeation chromatography using styrene as a standard reference material.

Monomers used in Resin Synthesis Examples are shown as follows:

Synthesis of Monomer A

A solution produced by dissolving Compound (XXI-1)(150 g) in dimethylformamide (622 g) was added dropwise to a slurry consisting of Compound (XXIII-1) (methacrylic acid, 61.6 g), potassium carbonate (134.8 g). Potassium iodide (45 g) was added thereto, and the mixture was stirred at a room temperature for 4.5 hours. The resulting reaction mixture was diluted by water, and then diluted mixture was extracted with ethyl acetate. The organic layer obtained was washed with water, dried by magnesium sulfate, decolorized by active carbon, then concentrated to obtain crystals of Monomer A (146.5 g, Yield: 80.4%).

m.p. 74.0–77.0° C.

NMR: 1.55–2.16 (4H, m) 1.98 (3H, s) 2.40–2.59 (2H, m) 3.22 (1H, m) 4.55 (1H, m) 4.66 (1H, m) 4.68 (2H, s) 5.69 (1H, m) 6.22 (1H, m)

FD-MS: m/z 280 (M+)

Synthesis of Intermediate for Monomer A

A solution produced by dissolving Compound (XXII-1)(chloroacetyl chloride, 159.3 g) in tetrahydrofuran (159 g) was added dropwise to a solution produced by dissolving Compound (XX-1) (145.0 g) and pyridine (89.3 g) in tetrahydrofuran (435 g) at 30° C. for an hour. After stirred at room temperature for 14 hours, the resulting reaction mixture was diluted by ethyl acetate. The diluted mixture was neutralized by 10% aqueous potassium carbonate solution, then crystals precipitated was collected by filtration and washed with water. The crude crystals obtained were dissolved in chloroform. The solution was dried with magnesium sulfate, decolorized with active carbon, then concentrated to obtain crystals of Compound (XXI-1) (155.8 g, Yield: 71.9%).

m.p. 147.0–149.0° C.

NMR: 1.62 (2H, m) 1.86 (1H, m) 2.02 (1H, m) 2.45 (1H, m) 2.50 (1H, m) 3.21 (1H, m) 4.39 (2H, s) 4.54 (1H, s) 4.58 (1H, m)

FD-MS: m/z 230 (M+)

RESIN SYNTHESIS EXAMPLE 1

Into a four-necked flask equipped with a thermometer and condenser, 82.46 parts of 1,4-dioxane was charged and bubbled with nitrogen gas for 30 min. In the nitrogen atmosphere, after the solvent was heated up to 87° C., a solution obtained by mixing 23.04 parts of Monomer A, 22.98 parts of Monomer B, 14.52 parts of Monomer D, 4.37 parts of Monomer H, 38.23 parts of Monomer K, 1.82 parts of azobisisobutyronitrile and 110.29 parts of 1,4-dioxane was added dropwise to the heated solvent for 2 hours with maintaining the temperature at 87° C. After the addition, the mixture was maintained at 87° C. for 6 hours. The reaction mixture was poured into a mixed solution of 857 parts of methanol and 214 parts of ion-exchanged water with stirring, the mixture was stirred, then the resin deposited in the mixture was collected by filtration. The deposit was added to 386 parts of methanol, the mixture was stirred, then the resin was collected by filtration. The series of operations comprising pouring, stirring and filtration was repeated two more times, and then dried under reduced pressure to obtain 55.2 parts of polymer having Mw (weight average molecular weight) of 7757 and Mw/Mn of 1.78. This is called resin R1.

RESIN SYNTHESIS EXAMPLES 2 TO 15

The reaction and after treatments were conducted in the same manner as in Resin Synthesis Example 1 except that monomers given in Table 1 were used in the ratio shown in Table 1 to obtain respective polymers shown in Table 1. Mw, Mw/Mn thereof and the ratio of each of monomers added were shown in Table 1.

RESIN SYNTHESIS EXAMPLE 16

Into a four-necked flask equipped with a thermometer and condenser, 25.81 g of Monomer A, 14.38 g of Monomer C, 2.30 g of azobisisobutyronitrile and 40.2 g of tetrahydrofuran were charged. In the nitrogen atmosphere, the charged mixture was maintained with stirring at 65° C. for 6 hours. The reaction mixture was cooled to room temperature, 40.2 g of tetrahydrofuran was added thereto. The added mixture was poured into a solution of 418 g of 2-propanol and 105 g of n-hexane. The polymer deposited was collected by filtration, and washed with small amount of n-hexane. The washed polymer was vacuum-dried to obtain white polymer. The polymer is called resin R16, which contains 39.4 mol % of a structural unit derived from Monomer A and 60.6 mol % of a structural unit derived from Monomer C, and which has Mw of 10151 and Mw/Mn of 2.13.

TABLE 1 Resin Monomers & Molar No. ratio of monomers Mw Mw/Mn R1 A/B/D/H/K = 20/25/20/5/30 7757 1.78 R2 A/B/J = 50/40/10 9321 1.82 R3 A/B/D/H/G = 25/35/10/10/20 8047 1.80 R4 A/C/H/K = 15/50/20/15 8593 1.74 R5 A/B/D/I/K = 18/32/18/9/23 7281 1.68 R6 A/C/E/G/H = 10/40/10/15/25 9205 1.79 R7 A/C/E/H = 25/40/10/25 10233 1.83 R8 A/B/D/H/K = 20/25/20/5/30 7779 1.78 R9 A/B/D/I/K = 20/35/10/10/25 6568 1.66 R10 A/B/H/L = 12.5/50/12.5/25 8590 1.74 R11 B/D/H/F/K = 25/20/20/5/30 8200 1.53 R12 C/H/K = 50/25/25 9721 1.53 R13 B/G/J = 30/60/10 10800 1.82 R14 A/M/H/K = 12/60/16/12 7468 1.92 R15 G/M/H = 20/60/20 8247 1.53 R16 A/C = 39/61 10151 2.13

EXAMPLES 1 TO 8 AND COMPARATIVE EXAMPLES 1 TO 5

The following components were mixed and dissolved, further, filtrated through a fluorine resin filter having pore diameter of 0.2 μm, to prepare resist liquid.

<Resin>

-   10 parts of Resin described in Table 1.     <Acid Generator> -   S1: 0.200 part of (4-methylphenyl)diphenylsulfonium     perfluorobutanesulfonate -   S2: 0.325 part of 1-(2-oxo-2-phenylethyl)tetrahydrothiophenium     perfluorobutanesulfonate     <Quencher> -   01: 0.325 part of 2,6-diisopropylaniline     <Solvent> -   Y1: 51.5 parts of propylene glycol monomethyl ether acetate, 35.0     parts of 2-heptanone and 3.5 parts of γ-butyrolactone -   Y2: 51.5 parts of propylene glycol monomethyl ether acetate, 35.0     parts of cyclohexanone and 3.5 parts of γ-butyrolactone

Silicon wafers were each coated with “ARC-29A-8”, which is an organic anti-reflective coating composition available from Brewer Co., and then baked under the conditions: 215° C., 60 seconds, to form a 780 Å-thick organic anti-reflective coating. Each of the resist liquids prepared as above was spin-coated over the anti-reflective coating so that the thickness of the resulting film became 0.25 μm after drying. The silicon wafers thus coated with the respective resist liquids were each prebaked on a direct hotplate at temperature shown in PB column in Table 2 for 60 seconds. Using an ArF excimer stepper (“NSR ArF” manufactured by Nikon Corporation, NA=0.55 σ=0.6), each wafer thus formed with the respective resist film was subjected to line and space pattern exposure, with the exposure quantity being varied stepwise.

After the exposure, each wafer was subjected to post-exposure baking on a hotplate at temperature shown in “PEB” column in Table 2 for 60 seconds and then to puddle development for 60 seconds with an aqueous solution of 2.38 wt % tetramethylammonium hydroxide.

Reflow Step was conducted by baking on a hotplate at 165° C. for 60 seconds after the development.

Each of a dark field pattern developed on the organic anti-reflective coating substrate after the development and before and after Reflow Step was observed with a scanning electron microscope, the results of which are shown in Table 3. The term “dark field pattern”, as used herein, means a pattern obtained by exposure and development through a reticle comprising chromium base surface (light-shielding portion) and linear glass layers (light-transmitting portion) formed in the chromium surface and aligned with each other. Thus, the dark field pattern is such that, after exposure and development, resist layer surrounding the line and space pattern remains on substrate.

Effective sensitivity:

It is expressed as the amount of exposure that the line pattern (light-shielding layer) and the space pattern (light-transmitting layer) become 1:1 after exposure through 0.16 cm line and space pattern mask and development.

Resolution:

It is expressed as the minimum size of space pattern which gave the space pattern split by the line pattern at the exposure amount of the effective sensitivity.

Line Edge Roughness

When line edge roughness is very good, its evaluation is marked by “⊚”

When line edge roughness is good, its evaluation is marked by “∘”.

When line edge roughness is bad, its evaluation is marked by “X”

Reflow

When pattern shape is greatly altered before and after Reflow Step, its evaluation is marked by “∘”.

When only top shape of pattern is altered, its evaluation is marked by “Δ”.

When no alteration on pattern is recognized, its evaluation is marked by “X”.

TABLE 2 Example Acid No. Resin Generator Quencher Solvent PB PEB Ex. 1 R1 S1&S2 Q1 Y1 110° C. 115° C. Ex. 2 R2 S1&S2 Q1 Y1 110° C. 115° C. Ex. 3 R3 S1&S2 Q1 Y1 110° C. 115° C. Ex. 4 R4 S1&S2 Q1 Y1 120° C. 125° C. Ex. 5 R5 S1&S2 Q1 Y1 110° C. 115° C. Ex. 6 R6 S1&S2 Q1 Y1 120° C. 125° C. Ex. 7 R7 S1&S2 Q1 Y1 120° C. 125° C. Ex. 8 R14 S1&S2 Q1 Y1 110° C. 100° C. Comp. Ex. 1 R11 S1&S2 Q1 Y1 110° C. 115° C. Comp. Ex. 2 R12 S1&S2 Q1 Y1 120° C. 125° C. Comp. Ex. 3 R13 S1&S2 Q1 Y1 110° C. 115° C. Comp. Ex. 4 R15 S1&S2 Q1 Y1 110° C. 100° C. Comp. Ex. 5 R16 S1&S2 Q1 Y2 130° C. 130° C.

TABLE 3 Effective Sensitivity Resolution Line Edge Example No. (mJ/cm²) (μm) Roughness Reflow Ex. 1 50 0.155 ⊚ ◯ Ex. 2 57.5 0.155 ◯ ◯ Ex. 3 52.5 0.15 ◯ ◯ Ex. 4 67.5 0.15 Δ Δ Ex. 5 45 0.155 ◯ ◯ Ex. 6 75 0.15 ◯ Δ Ex. 7 57.5 0.155 ◯ Δ Ex. 8 55 0.155 ◯ ◯ Comp. Ex. 1 45 0.155 Δ Δ Comp. Ex. 2 100 0.17 X X Comp. Ex. 3 50 0.15 X ◯ Comp. Ex. 4 100 0.165 X X Comp. Ex. 5 ** ** ** ** **: The wafer sample could not be resolved by 0.2 mm line and space pattern mask.

Apparent from the results shown in Table 3, while keeping equivalent or greater effective sensitivity and resolution, patterns obtained by Examples 1 to 8 which correspond to the present invention show better line edge roughness than those of Comparative Examples 1 to 5, and can be made finer by Reflow Step.

The chemically amplified positive resist composition of the present invention is suitable for excimer laser lithography using ArF, KrF and the like, and gives excellent resolution and sensitivity to resist pattern and excellent pattern shape and particularly, gives excellent line edge roughness. Moreover, the resist composition makes it possible to give finer pattern by Reflow Step. 

1. A chemically amplified positive resist composition comprising (A) a resin which comprises (i) at least one structural unit selected from the group consisting of structural units of the formulas (IV) and (V)

 wherein X³ and X⁴ each independently represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms, Z³ and Z⁴ each independently represents a divalent hydrocarbon group having 1 to 12 carbon atoms, n³ and n⁴ each independently represents an integer of 0 to 3, R² and R³ each independently represents a hydroxyl group or a hydroxymethyl group, G represents —(CO)O— or —O—, R⁴ represents an alkyl group having 1 to 4 carbon atoms or an alkoxy group having 1 to 4 carbon atoms, and p and q each independently represents an integer of 0 to 2, (ii) a structural unit of the formula (I)

 wherein X represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms, Z represents a divalent hydrocarbon group having 1 to 12 carbon atoms, R represents an alkyl group having 1 to 6 carbon atoms, and m represents an integer of 0 to 2, and (iii) a structural unit of the formula (II)

 wherein X¹ represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms, Z¹ represents a divalent hydrocarbon group having 1 to 12 carbon atoms, n¹ represents an integer of 0 to 3, R¹ represents an alkyl group having 1 to 6 carbon atoms or a cycloalkyl group having 3 to 12 carbon atoms, and Y represents at least two atoms necessary to form an alicyclic hydrocarbon group together with the adjacent carbon atom, and (B) an acid generator.
 2. The composition according to claim 1, which further comprises a structural unit of the formula (III)

wherein X² represents a hydrogen atom, an alkyl group having 1 to 4 carbon atoms or a perfluoroalkyl group having 1 to 4 carbon atoms, Z² represents a divalent hydrocarbon group having 1 to 12 carbon atoms, n² represents an integer of 0 to 3, and A represents a hydrocarbon group having 1 to 12 carbon atoms.
 3. The composition according to claim 1, wherein in the structural unit of the formula (IV), Z³ is a methylene group, an ethylene group, a trimethylene group or a tetramethylene group, n³ is 0 or 1, and p is 0 or 1, in the structural unit of the formula (V), Z⁴ is a methylene group, an ethylene group, a trimethylene group or a tetramethylene group, n⁴ is 0 or 1, R4 is a methyl group, an ethyl group, a methoxy group or an ethoxy group, and q is 0 or 1, in the structural unit of the formula (I), Z is a methylene group, an ethylene group, a trimethylene group or a tetramethylene group, and m is 0 or 1, and in the structural unit of the formula (II), Z¹ is a methylene group, an ethylene group, a trimethylene group or a tetramethylene group, n¹ is 0 or
 1. 4. The composition according to claim 1, wherein the structural unit of the formula (IV) is a structural unit of the formula (XIV)

wherein X¹⁰ represents a hydrogen atom, a methyl group or a trifluoromethyl group, n¹⁰ represents 0 or 1, and p′ represents 0 or 1, the structural unit of the formula (V) is a structural unit of the formula (XV)

wherein X¹¹ represents a hydrogen atom, a methyl group or a trifluoromethyl group, G represents —(CO)O— or —O—, and n¹¹ represents 0 or 1, in the structural unit of the formula (I), Z is a methylene group and m is 0, and in the structural unit of the formula (II), Z¹ is a methylene group, n1 is 0 or 1, Y is a divalent hydrocarbon group to form a divalent adamantane skeleton together with the adjacent carbon atom, a divalent hydrocarbon group to form a divalent norbornane skeleton together with the adjacent carbon atom, a tetramethylene group or a pentamethylene group.
 5. The composition according to claim 1, wherein the structural unit of the formula (IV) is a structural unit of the formula (XVIII)

wherein X¹² represents a hydrogen atom or a methyl group, and q′ represents 0 or 1, the structural unit of the formula (V) is a structural unit of the formula (XL)

wherein X¹³ represents a hydrogen atom or a methyl group, the structural unit of the formula (I) is a structural unit of the formula (XI)

wherein X⁶ represents a hydrogen atom, a methyl group or a trifluoromethyl group, and the structural unit of the formula (II) is a structural unit of the formula (XVII)

wherein X⁹⁰ represents a hydrogen atom or a methyl group, R⁹⁰ represents a methyl group, an ethyl group or an isopropyl group, and Y⁹⁰ is a divalent hydrocarbon group to form a divalent adamantane skeleton together with the adjacent carbon atom, a tetramethylene group or a pentamethylene group.
 6. The composition according to claim 2, wherein in the formula (III), X² is a hydrogen atom, a methyl group or a trifluoromethyl group, Z² is a methylene group, an ethylene group, a trimethylene group or a tetramethylene group, n² is 0 or 1, A is an alkyl having 1 to 5 carbon atoms, an alicyclic hydrocarbon group having 5 to 12 carbon atoms or an aromatic hydrocarbon group having 6 to 12 carbon atoms.
 7. The composition according to claim 2, wherein in the formula (III), X² is a hydrogen atom, a methyl group or a trifluoromethyl group, Z² is a methylene group, n² is 0 or 1, and A is a methyl group, an ethyl group, a n-propyl group, a n-butyl group, an isobutyl group, a tert-butyl group, a cyclopentyl group, a cyclohexyl group, a norbornyl group, an adamantly group or a decahydro-1,4:5,8-dimethanonaphtyl group. 